Became an indispensable engineering material for aerospace, Marine, chemical and petrochemical industries.
Titanium ranks 9th among the elements that constitute the Earths crust.
Density of titanium: 4.51g/cm.
Weight:57% of steel.
Strength to density ratio :
3.5 times that of stainless steel.
1.3 times that of aluminum alloy.
1.7 times that of magnesium alloy.
Brand:TA1、TA2、TA3、TA4、TA5、GradesF1、GradesF2、GradesF3、GradesF4、GradesF5、Ti1、Ti2、Ti3、Ti4、Ti5
Product | Specification | |
mm | Inch | |
Titanium Ingots | Φ30mm-Φ260mm | (1.17-10.23Inch) |
Titanium Plate |
80 mm x 1500mm x 2600mm
-
400mm x 1500mm x 2600mm
|
3.15 x 59 x 102 Inch.
-
15.7 x 59 x 102 Inch.
|
Titanium Plate-Heat Forging |
3mm x 800mm x 6000mm
-
12mm x 1560mm x 6000mm
|
0.12 x 31.5 x 236 Inch.
-
0.47 x 61.5 x 236 Inch.
|
Titanium Plate-Forging |
0.1mm x 350mm x Length
-
3.0mm x 1300mm x Length
|
0.00393 x 13.78 x Length Inch.
-
0.472 x 51.2 x Length Inch.
|
GB/T 39799-2024、GB/T 3620
ASTM B265、ASTM F136、ASTM F67、AMS4928
|
Titanium Sponge Production Process:
Smelting by VAR and EB furnace in two ways:
Titanium Ingot→ Forging → Plate → Rolling → Annealing → Titanium Coil → Strip → Testing→ packaging → Delivery.
Hot forging process: Performed above the recrystallization temperature of the metal.
5.5
~
6.75
3.5
~
4.5
0.12
~
0.25
2.5
~
3.5
2.0
~
3.0
0.2
~
0.4
0.6
~
0.9
Chemical
Composition
Grade
N
C
H
Fe
O
Al
V
Pa
Mo
Ni
Ti
Gr1
0.03
0.08
0.015
0.2
0.18
/
/
/
/
/
bal
Gr2
0.03
0.08
0.015
0.3
0.25
/
/
/
/
/
bal
Gr3
0.05
0.08
0.015
0.3
0.35
/
/
/
/
/
bal
Gr4
0.05
0.08
0.015
0.5
0.4
/
/
/
/
/
bal
Gr5
0.05
0.08
0.015
0.4
0.2
/
/
/
bal
Gr7
0.03
0.08
0.015
0.3
0.25
/
/
/
/
bal
Gr9
0.03
0.08
0.015
0.25
0.15
/
/
/
bal
Gr12
0.03
0.08
0.015
0.3
0.25
/
/
/
bal
Hot rolling:
Carried out at temperatures higher than recrystallization.
Cold rolling process:
Plastic deformation temperature is lower than the recovery temperature.
Annealing:
A metal heat treatment process in which the metal is slowly heated to a certain temperature, held for a sufficient time, and then cooled at a suitable rate.
Pickling:
The part is immersed in an aqueous solution such as sulfuric acid to remove the oxide film on the metal surface.
It is the pre-treatment or intermediate treatment of electroplating, enamel, rolling and other processes